PC/ABS物性表 

 
 
 
Bayblend T85
General purpose grades / Standard
Datasheet

General purpose injection molding grade; Vicat/B 120 temperature = 131°C; high impact and notched impact strength.
PC+ABS
 
ISO / ASTM
Date: 16.02.2004
 
 
Property
Test Condition
Standard
Unit:
Value
 
Rheological properties
 
 Spiral flow length
 260 °C; 2 x 8.7 mm
 Bayer test
 mm
 345
 C
 Melt volume-flow rate
 260 °C; 5 kg
 ISO 1133
 cm³/(10 min)
 12
 
 Molding shrinkage, parallel
 150x105x3; 260 °C / MT 80 °C; 500 bar
 based on ISO 2577
 %
 0.55 - 0.75
 
 Molding shrinkage, normal
 150x105x3; 260 °C / MT 80 °C; 500 bar
 based on ISO 2577
 %
 0.55 - 0.75
 
 
Mechanical properties (23 °C/50 % r.h.)
 C
 Tensile modulus
 1 mm/min
 ISO 527-1,-2
 MPa
 2300
 C
 Yield stress
 50 mm/min
 ISO 527-1,-2
 MPa
 55
 C
 Yield strain
 50 mm/min
 ISO 527-1,-2
 %
 4.7
 
 Stress at break
 50 mm/min
 ISO 527-1,-2
 MPa
 48
 
 Strain at break
 50 mm/min
 based on ISO 527-1,-2
 %
 > 50
 
 Izod impact strength
 23 °C
 ISO 180-1U
 kJ/m²
 N
 
 Izod impact strength
 -30 °C
 ISO 180-1U
 kJ/m²
 N
 
 Izod notched impact strength
 23 °C
 ISO 180-1A
 kJ/m²
 48
 
 Izod notched impact strength
 -30 °C
 ISO 180-1A
 kJ/m²
 38
 
 
Thermal properties
 C
 Temperature of deflection under load
 1.80 MPa
 ISO 75-1,-2
 °C
 109
 C
 Temperature of deflection under load
 0.45 MPa
 ISO 75-1,-2
 °C
 127
 C
 Vicat softening temperature
 50 N; 50 °C/h
 ISO 306
 °C
 129
 
 Vicat softening temperature
 50 N; 120 °C/h
 ISO 306
 °C
 131
 C
 Coefficient of linear thermal expansion, parallel
 23 to 55 °C
 ISO 11359-1,-2
 10-4/K
 0.75
 C
 Coefficient of linear thermal expansion, transverse
 23 to 55 °C
 ISO 11359-1,-2
 10-4/K
 0.8
 C
 Burning behavior UL 94
 0.85 mm
 UL 94
 Class
 HB
 
 
Electrical properties (23 °C/50 % r.h.)
 C
 Relative permittivity
 100 Hz
 IEC 60250
 -
 3.1
 C
 Relative permittivity
 1 MHz
 IEC 60250
 -
 3.0
 C
 Dissipation factor
 100 Hz
 IEC 60250
 10-4
 20
 C
 Dissipation factor
 1 MHz
 IEC 60250
 10-4
 85
 C
 Volume resistivity
 
 IEC 60093
 Ohm*m
 1E14
 C
 Surface resistivity
 
 IEC 60093
 Ohm
 1E16
 C
 Electric strength
 1 mm
 IEC 60243-1
 kV/mm
 35
 C
 Comparative tracking index CTI
 Solution A
 IEC 60112
 Rating
 225
 
 
Other properties (23 °C)
 C
 Water absorption
 Saturation value in water at 23 °C
 ISO 62
 %
 0.7
 C
 Water absorption
 Equilibrium value at 23 °C; 50 % RH
 ISO 62
 %
 0.2
 C
 Density
 
 ISO 1183
 kg/m³
 1150
 
 
Processing conditions for test specimens
 C
 Injection molding-Melt temperature
 
 ISO 294
 °C
 260
 C
 Injection molding-Mold temperature
 
 ISO 294
 °C
 80
 C
 Injection molding-Injection velocity
 
 ISO 294
 mm/s
 240

C  

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Bayblend FR 2000
FR grades / Non reinforced
Datasheet

Injection molding grade; easy-flow grade; Vicat/B 120 temperature = 95 °C; UL-listing 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test: 960 °C (2.0 mm); optimized processability; good light stability.
PC+ABS
 
ISO / ASTM
Date: 16.02.2004

 

 
Property
Test Condition
Standard
Unit:
Value
 
Rheological properties
 
 Spiral flow length
 260 °C; 2 x 8.7 mm
 Bayer test
 mm
 500
 C
 Melt volume-flow rate
 240 °C; 5 kg
 ISO 1133
 cm³/(10 min)
 26
 
 Molding shrinkage, parallel
 150x105x3; 240 °C / MT 80 °C; 500 bar
 based on ISO 2577
 %
 0.5 - 0.7
 
 Molding shrinkage, normal
 150x105x3; 240 °C / MT 80 °C; 500 bar
 based on ISO 2577
 %
 0.5 - 0.7
 
 
Mechanical properties (23 °C/50 % r.h.)
 C
 Tensile modulus
 1 mm/min
 ISO 527-1,-2
 MPa
 2700
 C
 Yield stress
 50 mm/min
 ISO 527-1,-2
 MPa
 60
 C
 Yield strain
 50 mm/min
 ISO 527-1,-2
 %
 4
 
 Stress at break
 50 mm/min
 ISO 527-1,-2
 MPa
 45
 
 Strain at break
 50 mm/min
 based on ISO 527-1,-2
 %
 > 50
 
 Izod impact strength
 23 °C
 ISO 180-1U
 kJ/m²
 N
 
 Izod notched impact strength
 23 °C
 ISO 180-1A
 kJ/m²
 35
 
 Izod notched impact strength
 -30 °C
 ISO 180-1A
 kJ/m²
 10
 
 
Thermal properties
 C
 Temperature of deflection under load
 1.80 MPa
 ISO 75-1,-2
 °C
 80
 C
 Temperature of deflection under load
 0.45 MPa
 ISO 75-1,-2
 °C
 90
 C
 Vicat softening temperature
 50 N; 50 °C/h
 ISO 306
 °C
 93
 
 Vicat softening temperature
 50 N; 120 °C/h
 ISO 306
 °C
 95
 C
 Coefficient of linear thermal expansion, parallel
 23 to 55 °C
 ISO 11359-1,-2
 10-4/K
 0.76
 C
 Coefficient of linear thermal expansion, transverse
 23 to 55 °C
 ISO 11359-1,-2
 10-4/K
 0.8
 C
 Burning behavior UL 94 (1.6 mm)
 1.5 mm
 UL 94
 Class
 V-0
 C
 Burning behavior UL 94-5V
 2.0 mm
 UL 94
 Class
 5VB
 
 Burning behavior UL 94-5V
 3.0 mm
 UL 94
 Class
 5VA
 
 
Electrical properties (23 °C/50 % r.h.)
 C
 Relative permittivity
 100 Hz
 IEC 60250
 -
 3.2
 C
 Relative permittivity
 1 MHz
 IEC 60250
 -
 3.1
 C
 Dissipation factor
 100 Hz
 IEC 60250
 10-4
 50
 C
 Dissipation factor
 1 MHz
 IEC 60250
 10-4
 70
 C
 Volume resistivity
 
 IEC 60093
 Ohm*m
 1E14
 C
 Surface resistivity
 
 IEC 60093
 Ohm
 1E16
 C
 Electric strength
 1 mm
 IEC 60243-1
 kV/mm
 30
 C
 Comparative tracking index CTI
 Solution A
 IEC 60112
 Rating
 350
 
 
Other properties (23 °C)
 C
 Water absorption
 Saturation value in water at 23 °C
 ISO 62
 %
 0.5
 C
 Water absorption
 Equilibrium value at 23 °C; 50 % RH
 ISO 62
 %
 0.2
 C
 Density
 
 ISO 1183
 kg/m³
 1180
 
 
Processing conditions for test specimens
 C
 Injection molding-Melt temperature
 
 ISO 294
 °C
 240
 C
 Injection molding-Mold temperature
 
 ISO 294
 °C
 80
 C
 Injection molding-Injection velocity
 
 ISO 294
 mm/s
 240

C  

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
拜耳PC/ABS FR2010 技術指標
 
性能
測試條件
單位
標準
數值
 流變性能
螺旋線流動長度
260℃,2*8.7mm
mm
 
415
熔融指數(MVR)
240℃ 
cm3/10min
ISO 1133
25
 
260℃
cm3/10min
ISO 1133
 
成型收縮率 流動方向
500 bar
%
 基於
0.4-0.6
垂直流動方向
500 bar
%
ISO 2577
0.4-0.6
 機械性能(23℃,50%相對濕度)
拉伸模量
1mm/min
MPa
ISO 527
2700
屈服應力
50mm/min
MPa
ISO 527
60
屈服應變
50mm/min
%
ISO 527
4
拉伸強度
50mm/min
MPa
ISO 527
50
斷裂延伸率
50mm/min
%
基於ISO 527
〉50
IZOD衝擊強度
23℃
  kj/m2
ISO180-1u
N
 
-30℃
kj/m2
ISO180-lu
 
IZOD缺口衝擊強度
23℃
kj/m2
ISO180-1A
35
 
-30℃
kj/m2
ISO180-1A
10
 熱性能
熱變形溫度 方法AF
1.80Mpa
℃ 
ISO75
90
方法BF
0.45Mpa
℃ 
ISO75
100
維卡軟化溫度
50N,50K/H
℃ 
ISO306
108
 
50N,120K/H
 
110
線形熱膨脹係數流動方向
23至/to 55℃
10-4/K
ISO11359-2
0.76
垂直流動方向
23至/to 55℃
10-4/K
 
0.80
可燒性實驗UL94
厚度:1.5mm
等級
UL94
V-O
可燒性實驗UL94-5V
厚度:2.0mm
等級
UL94
 
可燒性實驗UL94-5V
厚度:2.2mm
等級
UL94
5VB
可燒性實驗UL94-5V
厚度:2.4mm
等級
UL94
 
可燒性實驗UL94-5V
厚度:3.0mm
等級
UL94
5VA
 電性能
相對介電常數
100HZ
-
IEC60250
3.2
相對介電常數
1MHZ
-
IEC60250
3.1
損耗因子
100HZ
10-4
IEC60250
40
損耗因子
1MHZ
10-4
IEC60250
70
體積電阻率
 
Ω.cm
IEC60093
1E15
表面電阻率
 
Ω
IEC60093
1E14
介電強度
 
kv/mm
IEC60243-1
30
抗電弧徑跡性
溶液A
 等級 
IEC60112
350
其他性能
吸水性
   23;飽和值2
%
ISO62
0.5
吸濕性
  23℃ /50 ℃相對溫度 
 
%
基於ISO62
0.2
密度
 
kg/m3
ISO1183
1180
玻纖含量
-
%
ISO3451-1
 
測試試樣的工藝條件
熔體溫度
-
ISO294
240
模具溫度
-
ISO294
80
注射溫度
-
mm/s
ISO294
240
拜耳PC/ABS FR2010 技術指標
 
性能
測試條件
單位
標準
數值
 流變性能
螺旋線流動長度
260℃,2*8.7mm
mm
 
415
熔融指數(MVR)
240℃ 
cm3/10min
ISO 1133
25
 
260℃
cm3/10min
ISO 1133
 
成型收縮率 流動方向
500 bar
%
 基於
0.4-0.6
垂直流動方向
500 bar
%
ISO 2577
0.4-0.6
 機械性能(23℃,50%相對濕度)
拉伸模量
1mm/min
MPa
ISO 527
2700
屈服應力
50mm/min
MPa
ISO 527
60
屈服應變
50mm/min
%
ISO 527
4
拉伸強度
50mm/min
MPa
ISO 527
50
斷裂延伸率
50mm/min
%
基於ISO 527
〉50
IZOD衝擊強度
23℃
  kj/m2
ISO180-1u
N
 
-30℃
kj/m2
ISO180-lu
 
IZOD缺口衝擊強度
23℃
kj/m2
ISO180-1A
35
 
-30℃
kj/m2
ISO180-1A
10
 熱性能
熱變形溫度 方法AF
1.80Mpa
℃ 
ISO75
90
方法BF
0.45Mpa
℃ 
ISO75
100
維卡軟化溫度
50N,50K/H
℃ 
ISO306
108
 
50N,120K/H
 
110
線形熱膨脹係數流動方向
23至/to 55℃
10-4/K
ISO11359-2
0.76
垂直流動方向
23至/to 55℃
10-4/K
 
0.80
可燒性實驗UL94
厚度:1.5mm
等級
UL94
V-O
可燒性實驗UL94-5V
厚度:2.0mm
等級
UL94
 
可燒性實驗UL94-5V
厚度:2.2mm
等級
UL94
5VB
可燒性實驗UL94-5V
厚度:2.4mm
等級
UL94
 
可燒性實驗UL94-5V
厚度:3.0mm
等級
UL94
5VA
 電性能
相對介電常數
100HZ
-
IEC60250
3.2
相對介電常數
1MHZ
-
IEC60250
3.1
損耗因子
100HZ
10-4
IEC60250
40
損耗因子
1MHZ
10-4
IEC60250
70
體積電阻率
 
Ω.cm
IEC60093
1E15
表面電阻率
 
Ω
IEC60093
1E14
介電強度
 
kv/mm
IEC60243-1
30
抗電弧徑跡性
溶液A
 等級 
IEC60112
350
其他性能
吸水性
   23;飽和值2
%
ISO62
0.5
吸濕性
  23℃ /50 ℃相對溫度 
 
%
基於ISO62
0.2
密度
 
kg/m3
ISO1183
1180
玻纖含量
-
%
ISO3451-1
 
測試試樣的工藝條件
熔體溫度
-
ISO294
240
模具溫度
-
ISO294
80
注射溫度
-
mm/s
ISO294
240









 


網站首頁  |  產品目錄  |  供貨目錄  |  常用塑膠原料特性  |  代理拜耳公司PC/ABS  |  PC/ABS物性表  |  韓國科隆POM  |  塑膠原料最新報價  |  ABS SGS  |  最新消息  |  聯繫我們  |  網站地圖  |  手機版
  简体版     繁體版
Powered by DIYTrade.com